Products / Services : Anhui Safe Electronics Co., LTD.sales department

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

metalized capacitor film 1.with heavy-edge capacitor film 2.Al-Zn metallized capacitor film 3.Good tensile strength film

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!

Metallized BOPP film This metallized film is specially used for capacitors, power electronics capacitors, film capacitors,DC capacitor,AC capacitor and so on. Metallized BOPP film Cores Material:Plastic Width :Film Slit Width +/-0.3mm Inner Diameter:75mm +1.0mm/-0.5mm Specifications of metallized film Density :0.905+/-0.005 g/cm3 tensile Strength: >= 100 MD(MPa) Elongation at Break : 40 200 MD(%) Heat Shrinkage: <=5 ( 120C, 10min)( 120 C , 10 min )MD(%) Break-dowm voltage: >=350 ( 23 C, DC )V/um Coating square resistance: with heavy-edge area:3+/-1 without heavy-edge area: 7.5 +/-2.5 Dissipation Factor: <=4¡Á10-4 (20¡ãC,1KHz ) RC: >=5¡Á104 Main metallized film 1.Al Polypropylene film,Zn-Al Polypropylene film,Ag-Zn-Al Polypropylene film 2.Polyester film 3.High square resistance films 4.Gradient square resistance film 5.Safety explosion-proof film 6.BOPP base film for metalizing metallized film Storage Inner 1.The piled rolls are packed in plastic bag and heat-sealed with desiccants after vacuum removal 2.Labels inside the bags mark film class, type, thickness, width,free margin width and resistance. Outter 1.The bags are packed in carton cases. 2.The carton cases are packed in wooden cases or reinforced carton. 1. Metallized Film should be stored in 535 c and humidity less than 85% RH. 2.On exposure to moisture, the thin metallized layer is likely to be easily oxidized.Once opened, the rolls should be used as soon as possible. 3.It is rerecommend that the opened rolls be stored in temperature conditions of 15- 25 c and humidity of less than 60%RH. 4.Metallized Film kept sealed on the original packing and stored as described above is guaranteed according to the following conditions: 5.Al metallized film: 12 months from the delivered date. 6.Al/Zn Alloy metallized film: As Zn is relatively unstable,preservation period depends on the resistance of film. 7.10 Ohms or less: 6 months(from delivery date) 8.10 to 15 Ohms: 3 months(from delivery date) 9.15 Ohms: 1 month(from delivery date) NOTE:Unusual specification for capacitor film can be negotiated and specified additionally. For more products and information, please to contact us!